Submitted: 23 Jul 2013
Accepted: 18 Nov 2013
ePublished: 18 Nov 2013
EndNote EndNote

(Enw Format - Win & Mac)

BibTeX BibTeX

(Bib Format - Win & Mac)

Bookends Bookends

(Ris Format - Mac only)

EasyBib EasyBib

(Ris Format - Win & Mac)

Medlars Medlars

(Txt Format - Win & Mac)

Mendeley Web Mendeley Web
Mendeley Mendeley

(Ris Format - Win & Mac)

Papers Papers

(Ris Format - Win & Mac)

ProCite ProCite

(Ris Format - Win & Mac)

Reference Manager Reference Manager

(Ris Format - Win only)

Refworks Refworks

(Refworks Format - Win & Mac)

Zotero Zotero

(Ris Format - Firefox Plugin)

J Iran Dent Assoc. 2013;25(3): 198-202.
  Abstract View: 19

Original

Effect of Tea on Color Change of Silorane and Methacrylate based Composite Resins

Haleh Heshmat, Morvarid Hajian, Maryam Hoorizad Ganjkar*, Mansoreh Emami Arjomand
*Corresponding Author: Email: mahoorizad@yahoo.com

Abstract

   Background and Aim : At present, stainability and color instability of tooth-colored restorations following the consumption of colored beverages are among the problems commonly encountered in restorative dentistry. Filtek P90 composite resin comprising of Oxirane and Siloxanefunctional moietieswas recently introduced aiming at reducing the polymerization shrinkage. The aim of this study was to evaluate the effect of tea on color change of P90 and Z250 composite resins using spectrophotometry .

  Materials and Methods : For this experimental study, 20 composite discs were fabricated in metal molds from Z250 and P90 composite resins and light cured using LED light-curing unit. Specimens were stored in distilled water at 37 ° C for 24 hours to allow completion of polymerization. Color of specimens was then measured at baseline and after 5 days of storage in water and tea solution using spectrophotometer. Data were analyzed using independent sample t-test and two-way ANOVA .

  Results : The color change of P90 and Z250 composites after storage in distilled water was not significant in comparison to their baseline color (P>0.05). However, both composite resins showed a significant change in color after storage in tea solution (P<0.05). Stainability of Z250 composite in tea was significantly greater than that of P90 but in distilled water P90 showed greater color change than Z250 .

  Conclusion: Within the limitations of this study, Z250 composite demonstrated significantly greater color change in comparison to P90 after immersion in tea solution .

 

First Name
Last Name
Email Address
Comments
Security code


Abstract View: 20

Your browser does not support the canvas element.


PDF Download: 0

Your browser does not support the canvas element.