Submitted: 15 Nov 2015
Accepted: 15 Nov 2015
ePublished: 15 Nov 2015
EndNote EndNote

(Enw Format - Win & Mac)

BibTeX BibTeX

(Bib Format - Win & Mac)

Bookends Bookends

(Ris Format - Mac only)

EasyBib EasyBib

(Ris Format - Win & Mac)

Medlars Medlars

(Txt Format - Win & Mac)

Mendeley Web Mendeley Web
Mendeley Mendeley

(Ris Format - Win & Mac)

Papers Papers

(Ris Format - Win & Mac)

ProCite ProCite

(Ris Format - Win & Mac)

Reference Manager Reference Manager

(Ris Format - Win only)

Refworks Refworks

(Refworks Format - Win & Mac)

Zotero Zotero

(Ris Format - Firefox Plugin)

J Iran Dent Assoc. 2015;27(2): 90-96.
  Abstract View: 19

Original

Effect of Triple Antibiotic Paste on Bond Strength of Composite to Dentin: An In Vitro Study

Maryam Zare Jahromi* ORCID logo, Parvin Mirzakouchaki, Sanaz Mirsatari, Shadi Kazemi
*Corresponding Author: Email: m.zare@khuisf.ac.ir

Abstract

Background and Aim: Considering the increasing use of antibiotics in root canal therapy and the possible effects of intracanal medicaments on the bond strength of composite restorations, the aim of this study was to evaluate the effect of triple antibiotic paste (TAP) on shear bond strength of three types of composite resins to dentin.

Materials and Methods: In this in-vitro, experimental study, the enamel of 60 extracted premolars was ground parallel to the longitudinal axis of the teeth in order to produce flat dentin surfaces (5 mm2 minimum surface area). The samples were divided into six groups. In the control group, dentin surfaces were stored in saline solution and in the experimental groups dentin surfaces were exposed to TAP for 10 days. After washing and drying, Single Bond was applied for dentin bond to Z100 and Z350 composites. Adhesive resin was used for bond to P90 composite. Composites were applied on the dentin surfaces in six groups and cured in four directions. The shear bond strength was measured by Instron machine. The data were analyzed by t-test, one-way ANOVA and Tukey’s test.

Results: The highest mean shear bond strength was found in Z350 composite group following the use of TAP (38.75 MPa) and the lowest mean strength was found in Z100 composite group following the use of TAP (14.64 MPa). The mean shear bond strength of P90 and Z100 composites (in contrast to Z350 composite) was higher in the saline compared to the TAP groups (p=0.1). The differences between saline and antibiotic groups were not significant (p=0.959) but the difference in this regard among the three types of composites was significant.

Conclusion: The results of this study showed that use of TAP has no effect on the shear bond strength of composite to dentin but the type of composite significantly affects the shear bond strength.

First Name
Last Name
Email Address
Comments
Security code


Abstract View: 20

Your browser does not support the canvas element.


PDF Download: 0

Your browser does not support the canvas element.