Submitted: 30 Apr 2007
Accepted: 25 Feb 2013
ePublished: 25 Feb 2013
EndNote EndNote

(Enw Format - Win & Mac)

BibTeX BibTeX

(Bib Format - Win & Mac)

Bookends Bookends

(Ris Format - Mac only)

EasyBib EasyBib

(Ris Format - Win & Mac)

Medlars Medlars

(Txt Format - Win & Mac)

Mendeley Web Mendeley Web
Mendeley Mendeley

(Ris Format - Win & Mac)

Papers Papers

(Ris Format - Win & Mac)

ProCite ProCite

(Ris Format - Win & Mac)

Reference Manager Reference Manager

(Ris Format - Win only)

Refworks Refworks

(Refworks Format - Win & Mac)

Zotero Zotero

(Ris Format - Firefox Plugin)

J Iran Dent Assoc. 2006;18(1): 97-104.
  Abstract View: 24

Research

Comparison of sealing ability of Coltozol, Portland cement, Amalgam and MTA in furcation perforations repair

Zohreh Ahangari*, Mahdiyeh Karami
*Corresponding Author: Email: zohreh_ahangari@yahoo.com

Abstract

Comparison of sealing ability of Coltozol, Portland cement, Amalgam and MTA in furcation perforations repair

 Dr. Z. Ahangari* - Dr. M. Karami**

 *- Associate Professor of Endodontics Dept. - Faculty of Dentistry – Shaheed Beheshti University of Medical Sciences.

 **- Dentist.

 Background and Aim: The rate of treatment success in endodontic treatment if perforation of the pulpal floor occurs, due to secondary periodontal involvement, is not satisfactory. Therefore, perforation seal plays an important role in regional repair. The aim of this study was to investigate and select a more suitable material to seal furcal perforations.

Materials and Methods: In this experimental study, 70 human permanent mandibular molars with non-fused roots and intact furcal region were collected. Access openings and furcation perforations were prepared in the pulpal chamber floor. The teeth were divided into two control groups (B1 – B2, negative and positive, n = 5) and four experimental groups of 15 teeth in each group (A1 – A2 – A3 – A4). Group A2 was repaired with MTA, group A2 with amalgam, group A3 with Coltozol (ZOE) and group A4 was repaired with Portland cement. The access cavities of all teeth were repaired with Coltozol. Then, all samples were thermocycled for 24 hours and submerged in solution of 2% fuchsin dye for 24 hours. No cavity was prepared in negative control group. Finally, the samples were sectioned and evaluated for linear dye leakage at ×25 magnification. Data were analyzed using LSD and ANOVA tests.

Results: In positive control group, dye penetrated thoroughly in all perforation regions while no leakage was observed in negative control group. MTA had significantly less leakage than amalgam, Portland cement and Coltozol. The highest leakage was found in Coltozol group and the difference with amalgam and MTA was significant (P<0.01). Amalgam showed less leakage than Portland cement but the difference was not statistically significant, however the difference between Portland cement and MTA in the amount of leakage was significant (P<0.01).

Conclusion: MTA group showed the least microleakage while Coltozol group displayed the most. In this study, the four materials were ranked as follows: MTA, Amalgam, Portland cement, Coltozol.

Key words: Furcal perforations – Microleakage - Repair

First Name
Last Name
Email Address
Comments
Security code


Abstract View: 25

Your browser does not support the canvas element.


PDF Download: 0

Your browser does not support the canvas element.