Submitted: 23 May 2007
Accepted: 25 Feb 2013
ePublished: 25 Feb 2013
EndNote EndNote

(Enw Format - Win & Mac)

BibTeX BibTeX

(Bib Format - Win & Mac)

Bookends Bookends

(Ris Format - Mac only)

EasyBib EasyBib

(Ris Format - Win & Mac)

Medlars Medlars

(Txt Format - Win & Mac)

Mendeley Web Mendeley Web
Mendeley Mendeley

(Ris Format - Win & Mac)

Papers Papers

(Ris Format - Win & Mac)

ProCite ProCite

(Ris Format - Win & Mac)

Reference Manager Reference Manager

(Ris Format - Win only)

Refworks Refworks

(Refworks Format - Win & Mac)

Zotero Zotero

(Ris Format - Firefox Plugin)

J Iran Dent Assoc. 2004;16(4): 53-60.
  Abstract View: 16

Research

An investigation on the adhesion of two endodontic sealers‌ ‌AH 26, Dorifill) to dentin (

Sedigheh Khedmat*, Mahmood Khorramdoost
*Corresponding Author: Email:

Abstract

An investigation on the adhesion of two endodontic sealers‌ ‌AH 26, Dorifill) to dentin (

* - Dr. S. Khedmat** Dr. M. Khorramdoost

*- Assistant professor of Endodontics Dept. Faculty of Dentistry Tehran University of Medical Sciences.

** - Dentist.

Background and aim: Tensile bond strength of endodontic sealers to dentin is an indicative of sealer's adhesion to dentin. Due to the fact that Gutta-percha is not bonded to dentin walls, the adhesion of a root canal sealer to dentin is an important issue in endodontics. The goal of this study was to compare the tensile bond strength of two sealers, AH26 and Dorifill, with dentin.

Materials and Methods: In this experimental study,30 extracted human first and second molars, with no occlusal carries, were stored in 0.9% Nacl. The enamel was removed 1mm below the central occlusal groove. The roots were cut at 2 mm below the CEJ. Wire hooks, made of orthodontic wire (0.5mm), were fixed to dentin surfaces and sealers. Aluminum cylinders were used to place sealer on the dentin surface and stabalized with two drops of wax. Two groups of sealers (AH26, Dorifill) Were placed within the cylinders (n=51). The lower end of the wire hook was lowered into the soft unset sealer. After 24 hours, wax drops were removed and each specimen was tested by zwick tester at the speed of 2mm/min. Data were subjected to Independent samples t-test. 0.04 Mpa±135 Mpa for AH26 and 0.0.383

Results: The mean tensile bond strength values were 1.885 Dorifill than Dorifill attributing higher tensile bond strenght to AH26 for

Conclusion: Applying AH26 in root canal therapy would be more successful than dorifill.

Key Words: Endodontic sealer-Dentin - Tensile bond strength.

First Name
Last Name
Email Address
Comments
Security code


Abstract View: 17

Your browser does not support the canvas element.


PDF Download: 0

Your browser does not support the canvas element.